Functional biodegradable polymers

ABSTRACT

Biodegradable polyesters are made by synthesizing copolymers derived from biodegradable hydroxyacid monomers as well as from hydroxyacid monomers containing a functional group such as an azide group, a halogen group, a thioacetate group, and the like. Preferably, the functionalized biodegradable polyester copolymers are derived from a functionalized hydroxyacid such as a homolog of lactic acid and/or glycolic acid with the copolyester thus containing functional groups on the backbone thereof. These biodegradable polyesters can be utilized wherever biodegradable polyesters are currently used, and also serve as a polymer to which various medical and drug delivery systems can be attached.

CROSS REFERENCE

This patent application claims the benefit and priority of U.S. provisional application 61/368,413, filed Jul. 28, 2010 for FUNCTIONAL BIODEGRADABLE POLYMERS, which is hereby fully incorporated by reference.

GOVERNMENT RIGHTS

The Government may have certain rights in this invention under National Science Foundation Contract No. DMR-0830301 and/or under National Health Institute Contract No. ARRA Supplement for Parent Grant 5RO1 GM86895-2.

FIELD OF THE INVENTION

The present invention relates to biodegradable polyester polymers or copolymers containing functionalities on their backbone that are capable of being covalently attached to compounds such as drugs or other therapeutic molecules for making drug delivery medications, or other small molecules of interest. More specifically, the invention relates to forming functionalized biodegradable polyesters or copolyesters derived from biodegradable hydroxyacid monomers and functional monomers.

BACKGROUND OF THE INVENTION

Traditional biodegradable polymers, like poly(lactic acid) (PLA), poly(glycolic acid) (PGA) and their copolymers (PLGA), see FIG. 1, do not have functionalities on their backbones. Such biodegradable polymer systems are therefore not able to covalently attach drugs or other therapeutic molecules for making drug delivery devices, or other functional molecules for a variety of applications. Instead, the functional molecules, such as therapeutic agents have to be physically entrapped into these polymers, either by forming micelles or by nano-encapsulation.

Recently, much attention has focused on the development of degradable and bioabsorbable polymers for biomaterials, and disposable or non-recoverable polymer goods applications. Biodegradable plastics we able to replace non-biodegradable polymers like polystyrene and poly(ethylene terephthalate) (PET) in a variety of applications. For example, Cargill Dow LLC under the trade name Nature Works is using PLA to make biodegradable products like dairy containers, food trays, cold drink cups, products for packaging applications, bottles for fruit juices, sport drinks and jams and jellies; poly(butylene succinate) is being used in agricultural applications in the form of mulch films, bags for seedlings and replanting pots; poly(butylene succinate) is also being used for manufacturing packaging films, bags and flushable feminine hygiene products because of its excellent mechanical properties. Traditional biodegradable polymers have included polyamides, polyanhydrides, polycarbonates, polyesters, polyesteramides, and polyurethanes, which incorporate a degradable linkage into the backbone that can be cleaved by hydrolytic, enzymatic and oxidative processes. Of these, aliphatic polyesters, specifically poly(lactic acid) (PLA), poly(lactic-co-glycolic acid) (PLEA) and poly(ε-caprolactone) (PCL), have become the most widespread biomedical soft materials, finding use in drug and gene delivery, sutures, stents, dental implants and as tissue engineering scaffolding. Aliphatic polyesters have found success due to their ease of preparation, good mechanical properties and relatively quick in vivo degradation to small molecules easily absorbed or excreted by the body. However, PLA, PLGA and PCL lack pendant functional groups, which is a major limitation for a large number of applications. Pendant functionality is highly desirable for the fine-tuning of properties such as rate of crystallization, fire retardancy, color, hydrophobicity, bioadhesion, biodegradability and the loading of therapeutics. Because of this, it is of great importance that an efficient route to main-chain functionalization of aliphatic polyesters and their random, graft, or block copolymers be found.

Polyesters are generally prepared by polycondensation of diols with diacids (A-A monomers+B-B monomers), self-condensation of hydroxyacids (A-B monomers), or by ring-opening polymerization of lactones. However, many useful functional groups, e.g. hydroxyl thiol, amine and carboxylic acid, are incompatible with these types of polymerization as they form cross-links, eliminating the functionality. Protecting group chemistry, chemoselective step-growth polymerization and ring-opening polymerization of monomers with non-reactive functional groups have all been used to address this problem to varying degrees of success to prepare polyesters with hydroxyl, thiol, ketone, halogen, azido, alkyne and poly(ethylene glycol) (PEG) pendant groups. However, no highly versatile and general strategy for functionalizing aliphatic polyesters has yet been developed.

2-Halo-3-hydroxypropionic acid (HHPA) is a halogenated constitutional isomer (C₃H₅XO₃) of LA (C₃H₆O₃), with a primary alcohol like GA (C₂H₄O₃), and is therefore an ideal co-monomer for incorporation of α-halo ester functionality into PLGA, PLA, PGA and/or their copolymers with other classes of polymers, including both condensation and addition polymers. Such polyesters are potentially biodegradable, and can be further functionalized post-polymerization, via nucleophilic substitution, radical addition, radical-radical coupling and/or electrophilic substitution.

α-Halo are activated to nucleophilic attack by three mechanisms: inductive electron withdrawal by the adjacent carbonyl, reduced steric bulk at the σ* orbital of the carbon-halogen bond due to the adjacent carbonyl and through-space electron donation from the σ-orbital of the carbon-halogen bond to the π* orbital of the carbonyl. Because of this activation, α-halo esters undergo nucleophilic substitution by a number of hard (e.g. alcohol, alkoxide, carboxylate and primary amine), soft (e.g. cyanide, iodide, thio and thioalkoxide) and borderline hard/soft nucleophiles (e.g. azide, nitroxide and pyridine) under mild conditions. The major hurdle to this type of reaction is chain scission due to attack at the carbonyl or α-elimination. For these reasons, very reactive/hard nucleophiles such as alkoxide or carbanions may not be suitable for this type of reaction.

α-Halo esters participate in electrophilic substitution reactions via lithium metalation, Grignard and Reformatsky chemistries. Of these, Reformatsky reactions are the most mild and therefore, potentially of the most useful. The classical Reformatsky reaction involves the coupling of an α-haloester with an electrophile, via a zinc enolate intermediate. First, zinc reacts with an α-haloester, by insertion into the carbon-halogen bond, to form an enolate. This enolate is then reacted with an electrophile, traditionally an aldehyde or ketone but also an anhydride, phosphonate or α,β-unsaturated carbonyl.

α-Halo esters participate in radical reactions due to the weakness of the carbon-halogen bond, which undergoes homolytic cleavage under redox conditions to form a carbon centered radical. Curran et al. [Synthesis 1988, 489-513] and Matyjaszewski et. al. have shown that α-halo esters can add across the double bond of an olefin in atom transfer radical coupling and polymerization reactions, respectively. Depending on the structure of the olefin this can impart new functional groups onto the polymer. Jerome et. al. have used ring-opening of α-chloro lactones to prepare chloro functional polyesters. They further derivatized these polyesters by coupling with 3-butenyl benzoate to demonstrate radical coupling and using them as macroinitiators for the atom transfer radical polymerization (ATRP) of methacylate to prepare graft copolymers. Depending on the location of the α-halogen the architecture of the system can be controlled. If the halogen is spread throughout the polymer backbone, grafting-to or grafting-from structures can be made. If the halogen is at the chain end then block copolymers can be readily made.

SUMMARY OF THE INVENTION

Biodegradable polyesters containing functional groups on their, backbone are generally prepared by two different routes. One route relates to the co-polyesterification of various hydroxyacid monomers and other monomers containing functional groups therein via a two-step route initially utilizing high temperature, low pressure and a catalyst and subsequently a linking agent, a different catalyst and ambient temperatures. The second route relates to a co-polyesterification of various hydroxyacid monomers and the functionalized monomers in the presence of an acid catalyst, high temperatures, and low pressures.

The use of 2-halo-3-hydroxypropionic acid as a co-monomer with a diol plus diacid system or a hydroxyacid, preferably GA and/or LA, incorporates halogen functionality therein and produces high molecular weight halogenated polyesters, by direct polycondesation. The co-polycondensation is acid catalyzed and driven by high temperature, e.g. from about 50° C. to about 180° C., and preferably from about 90° C. to about 110° C., and vacuum, e, g, from about 0 mm Hg to about 50 mm Hg and preferably from about 0 mm Hg to about 3 mm Hg. A small amount of high boiling solvent, preferably diphenylether (DPE) is used to plasticize the bulk. Copolymers with various compositions of LA, GA and 2-bromo-3-hydroxypropionic acid (BHPA) were prepared with number-average molecular weights of 2,000 to 40,000 Da relative to polystyrene (Da_(PSt)), preferably about 8,000 to about 20,000 Da_(PSt) (FIG. 5, FIG. 9, Table 1). To investigate potential reactions to functionalize the brominated polyester, a small molecule model compound, methyl 3-acetoxy-2-bromopropanoate (MABP), was synthesized and derivatized by nucleophilic substitution with sodium azide, sodium iodide and sodium thioacetate. Adapting from these conditions, the brominated polyester was functionalized into azido, iodo and thioester derived polyesters (FIG. 10). Further functionalization reactions were performed on the iodinated polyester.

In one aspect of the invention, a functionalized biodegradable copolyester is disclosed, comprising repeat units derived from one or more diode containing from 2 to about 10 carbon atoms and one or more dicarboxylic acids containing from 2 to about 15 carbon atoms, or repeat units derived from one or more hydroxyacids containing from 2 to about 20 carbon atoms, or both; repeat units derived from one or more functionalized hydroxyacids; and wherein said copolyester is a random, statistical copolymer and is biodegradable.

In another aspect of the invention, a process for synthesizing a functionalized biodegradable copolyester is disclosed comprising the steps of reacting one or more diols containing from 2 to about 10 carbon atoms with 1 one or more dicarboxylic acids containing from 2 to about 15 carbon atoms, or reacting one or more hydroxyacids containing from 2 to about 20 carbon atoms, or both; with one or more functionalized hydroxyacids at low pressure and elevated temperature in the presence of a protonic acid catalyst or a Lewis acid catalyst.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates poly(lactic acid-co-glycolic acid) copolymer;

FIG. 2 illustrates 2-halo-3-hydroxypropionic acid (HHPPA);

FIG. 3 illustrates synthesis of 2-halo-3-hydroxypropionic acid from DL-Serine;

FIG. 4 illustrates direct polycondensation of 2-halo-hydroxypropionic acid;

FIG: 5 illustrates co-polyesterification of 2-bromo-3-hydroxypropionic acid glycolic acid and/or lactice acid via a multi-step process;

FIG. 6 illustrates N,N′-Diisopropylcarbodiimide;

FIG. 7 illustrates 4-(dimethylamino)pyridinium 4-toluenesulphonate

FIG. 8 illustrates N,N′-Diisopropylurea;

FIG. 9 illustrates direct polycondensation of glycolic acid, lactic acid and 2-halo-3-hydroxypropionic acid;

FIG. 10 illustrates iodide, azide and thioacetate functionalization reactions on the model small molecule; and

FIG. 11 illustrates a reaction of a rearranged copolyester with sodium azide and with a thioacetate.

DETAILED DESCRIPTION OF THE INVENTION

The invention is initially described with respect to specific monomers and reaction conditions and then subsequently with regard to overall reaction conditions and compounds.

Biodegradable polyesters are made by synthesizing copolymers derived from biodegradable hydroxyacid monomers as well as from hydroxyacid monomers containing a functional group such as an azide group, a halogen group, a thioacetate group, and the like. Alternatively, or in addition thereto, biodegradable polyesters can be made from various diols having from 2 to about 10 carbon atoms and desirably from about 2 to about 3 carbon atoms and dicarboxylic acids having from about 2 to about 15 carbon atoms, desirably from about 2 to about 10 carbon atoms and preferably from about 2 to about 8 carbon atoms. Preferably, the functionalized biodegradable polyester copolymers are derived from a functionalized hydroxyacid such as a homolog of lactic acid and/or glycolic acid with the copolyester thus containing functional groups on the backbone thereof. Synthesized 2-halo-3-hydroxypropionic acids can be utilized as the key intermediate for the synthesis of acrylate-based inimers that can be polymerized by atom transfer radical polymerization or functionalized and polymerized by reversible addition-fragmentation chain transfer (RAFT) polymerization to produce hyperbranched polyacrylates, 2-Halo-3-hydroxypropionic acid is essentially a functionalized constitutional isomer of lactic acid (LA), and can therefore be used to synthesize halogenated poly(lactic acid), poly(glycolic acid), poly(lactic-co-glycolic acid) (PLGA), and other halogenated polyesters and condensation polymers in which the halogen can be used as a backbone attachment site for a compound such as a drug, therapeutic compound, antibody, peptide, nucleating agent, fire retardant, or other molecule of interest to the biodegradable, FDA-approved PLGA backbone. 2-Halo-3-hydroxypropionic acid (FIG. 2) is synthesized by a deaminohalogenation reaction of D-, L- or D,L-serine (FIG. 3). This monomer is a hydroxyacid, which can self-condense under acidic conditions to form oligo(halohydroxypropionic acid) (FIG. 4). This reaction is driven by applying heat and vacuum, to produce oligomers of number average molecular weight, M_(n)≧1,500 Da. By a polyesterification reaction, the halohydroxypropionic acid monomer is also copolymerized with lactic acid, glycolic acid and other hydroxyacids to form random, statistical copolymers. This polyesterification (FIG. 5) can be performed at high temperature and low pressure with subsequent polymerization occurring with a linking agent at room temperature under dry conditions using dichloromethane as a solvent, diisopropylcarbodiimide (DiPC) (FIG. 5) as the linking agent and dimethylaminopyridinium toluenesulphonate (DPTS) (FIG. 7) as the catalyst, After the reaction, the byproduct, diisopropylurea (DiPU) (FIG. 8) and the catalyst, DPTS, are washed out with a methanol/water mixture and the polymer is precipitated out in isopropyl alcohol (IPA) or in hexane/methanol (95%, 5%, v %, v %) mixture. Typical M_(n) of about 8,000-10,000 Da are obtained.

The co-polyesterification of the halohydroxypropionic acid with lactic acid and glycolic acid can also be performed in bulk using p-toluenesulphonic acid (PTSA) as a catalyst (FIG. 9). This reaction is driven by applying heat and vacuum and a typical M_(n) of ≧5,000 Da is observed.

The functionalized 2-halo-3-hydroxypropionic acid (HHPPA) is produced by reacting serine with an alkali nitrite such as sodium nitrite in the presence of an aqueous acid, preferably hydrobromic acid or hydrochloric acid, and potassium bromide or potassium chloride initially at low temperatures such as from about minus 35° C. to about 0° C. and preferably from about minus 15° C. to about minus 5° C. for short periods of time, such as from about 1 to about 6 hours and desirably from about 1.5 to about 2.5 hours until the addition of HX/KX to serine is complete. Subsequently, the reaction is continued at from about 5° C. to about 60° C., and desirably from about 15° C. to about 40° C., and most preferably from about 20° C. to about 30° C. for about 1 to about 48 hours and desirably from about 5 to about 24 hours, and most preferably from about 10 to about 14 hours to produce the halogenated hydroxyacid, i.e. HHPPA. Other hydroxy-containing amino acids such as tyrosine can also be used in this reaction.

HHPPA can be polymerized under high temperature and low pressure in the presence of a catalyst to produce a polymer as set forth in FIG. 4. That is, under acidic conditions as in the presence in p-toluenesulfonic acid, SnCl₂, or SnO, HHPPA can self-condense at temperatures of from about 50° C. to about 180° C. and desirably from about 80° C. to about 150° C., and most preferably from about 90° C. to about 110° C. at low pressures of from about 0 mm Hg to about 50 mm Hg and desirably from about 0 mm Hg to about 10 mm Hg, and most preferably from about 0 mm Hg to about 3 mm Hg in the presence of an acid catalyst such as p-toluenesulfonic acid, SnCl₂, or SnO, and the like. The resulting polymer generally has a number average molecular weight of at least about 2,000 desirably from about 6,000 to about30,000, and most preferably from about 20,000 to about 25,000 Da.

HHPPA and other functional-containing hydroxyacid monomers can be utilized to form biodegradable copolyesters by two different routes, for example co-polyesterification or by bulk polymerization of hydroxyacid monomers.

Examples of hydroxyacids that are nitrogen free, have a total of from 2 to about 20 carbon atoms and desirably 2 or 3 carbon atoms and contain at least 1 hydroxyl group include glycolic acid, galactaric acid, hydroxypropionic acid, lactic acid, hydroxybutyric acid, hydroxyisobutyric acid, hydroxy methylbutyric acid bis(hydroxymethyl)propionic acid, gibberellic acid, hydnoxyactadecanoic acid, di-tert-butyl hydroxybenzoic acid, benzilic acid, hydroxyl fluorenecarboxylic acid, hydroxydecanoic add, hydroxynaphthalenecarboxylic acid, hydroxybenzenedicarboxylic acid, hydroxymethylbenzoic acid, hydroxyphenylacetic acid, mandelic acid, hydroxymethoxybenzoic acid, methoxysalicylic acid hydroxyoctanoic acid, hydroxycinnamic acid, dihydroxycinnamic acid, dihydroxyhydrocinnamic acid, hydroxyphenylpropionic acid, dihydroxytartaric acid, hydroxymethoxycinnamic acid, salicylic acid, citrazinic acid, galacturonic acid, glucuronic acid, hydroxypropanedioic acid, hydroxyphenyl propionic acid, lactic acid, methoxysalicylic acid, tartaric acid, or trihydroxybenzoic acid, or any combination thereof. Lactic acid and glycolic acid are preferred. The above hydroxyacids that can be functionalized can be utilized, of course, as functionalized monomers. Examples of such functionalized mononers include chlorohydroxybenzoic acid, chloromandelic acid, chlorosalicylic acid, dibromo hydroxybenzoic acid, dichlorohydroxy-benzoic acid, dichlorosalicylic acid, or any combination thereof.

The HHPPA monomer and other functionalized acids can be reacted with various functional groups such as a halogen, an azide, a thioacetate, and the like in a manner well known to the art and to the literature. Upon reaction of the functionalized hydroxyacid, copolyesters are produced wherein a functional group is located on the backbone of the polymer.

The multi-step polyesterification route as set forth in FIG. 5 produces a statistical copolymer. The initial step is carried out at high temperatures, generally from about 50° C. to about 180° C., desirably from about 80° C. to about 150° C. and preferably from about 90° C. to about 110° C. Low pressures are utilized such as from about 0 mm Hg to about 50 mm Hg, desirably from about 0 mm Hg to about 10 mm Hg and preferably from about 0 mm Hg to about 3 mm Hg. Protonic or Lewis acids are utilized with specific compounds including p-dimethylaminopyridinium toluenesulphonate (DPTS), p-toluidine hydrochloride, dimethyl-p-phenylenediamine dihydrochloride, p-toluenesulphonic acid, and the like with p-toluenesulphonic acid being preferred. The amount of catalysts is generally small and ranges from about 0.01 equivalents to about 1.0 or to about 5 equivalents and desirably from about 0.03 equivalents to about 0.5 equivalents, and most preferably from about 0.05 equivalents to about 0.1 equivalents based upon the total equivalents of all hydroxyacid monomers. These reaction conditions generally produce a prepolymer, see FIG. 5. The prepolymer generally has the number average molecular weight of from about 2,000 Da to about 20,000 Da, desirably from about 4,000 Da to about 10,000 Da, and preferably from about 6,000 Da to about 9,000 Da. The reaction times will vary from about 2 hours to 48 hours, desirably from about 8 hours to 24 hours, and preferably from about 12 hours to 18 hours.

A subsequent step utilizes various solvents that include halogenated solvents such as dichloromethane and chloroform, polar solvents such as N,N-dimethylformamide, ether solvents such as tetrahydrofuran and aromatic solvents such as toluene, see FIG. 5. Dichloromethane and tetrahydrofuran are preferred. Suitable amounts of solvents are generally such that the various monomers can be readily dissolved and generally involve concentrations of from about 0.1 M to about 2 M and desirably from about 0.2 M to about 1.5 M, and most preferably from about 0.7 M to about 1 M.

Activating and dehydrating linking agents generally include carbodiimides with specific examples including diisopropylcarbodiimide, dicyclohexylcarbodiimide and ethyl-3-(3-dimethylaminopropyl)carbodiimide. Suitable amounts of linking agents generally range from about 0.5 equivalents to about 10 equivalents and desirably from about 1 equivalent to about 5 equivalents, and most preferably from about 1.1 equivalents to about 1.5 equivalents based upon the total equivalents of the prepolymer. The linking agents are added to the reaction at a temperature from about 0° C. to about 50° C. and desirably from about 0° C. to about 25° C. and most preferably from about 0° C. to about 5° C. The subsequent reaction is generally carried out at an ambient temperature of from about 10° C. to about 50° C., desirably from about 15° C. to about 35° C., and preferably from about 20° C. to about 30° C. for about 0.5 hours to about 24 hours and desirably from about 4 hours to about 7 hours. Catalysts for the subsequent reaction generally include protonic and latent protonic acids with specific compounds including p-dimethylaminopyridinium toluenesulphonate (DPTS), p-toluidine hydrochloride, dimethyl-p-phenylenediamine dihydrochloride, and the like with p-dimethylaminopyridinium toluenesulphonate being preferred. The amount of catalysts is generally small and ranges from about 0.01 equivalents to about 1.0 or to about 5 equivalents and desirably from about 0.03 equivalents to about 0.5 equivalents, and most preferably from about 0.05 equivalents to about 0.1 equivalents.

The reaction times are generally for about 30 minutes to 24 hours and desirably from about 2 hours to 12 hours, and most preferably from about 4 hours to 7 hours.

The resultant statistical polyester copolymer generally has a number average molecular weight of from about 2,000 Da to about 40,000 Da, desirably from about 5,000 Da to about 32,000 Da, more desirably from about 6,000 to about 25,000 Da, and preferably from about 8,000 Da to about 20,000 Da. After the reaction, various byproducts such as diisopropylurea and the catalyst are washed out of the reaction medium by utilizing a mixture of water and alcohol such as methanol with the polymer being subsequently precipitated as by utilizing a different alcohol such as isopropyl alcohol. The yield of the above described process is generally high, such as from at least about 10 mole %, generally at least about 50 mole %, and preferably at least about 90 mole % of all of said hydroxyacid monomers and functionalized monomers being incorporated into a polymer.

The functionalized biodegradable polyester copolymers derived utilizing the esterification route set forth in FIG. 5 will have repeat units generally in proportion to the amount of monomers utilized, with the repeat units derived from the functionalized hydroxyacids containing a functional group on the backbone thereof. If a biodegradable polyester copolymer having high functionality is desired, the amount of the one or more functionalized hydroxyacid, e.g. “n” is generally from about 10 or about 20 to about 99 mole %, desirably from about 30 to about 80 mole %, and most preferably from about 35 to about 60 mole %, with the amount of the one or more biodegradable monomers, e.g “l” and “m” being the difference. When lactic acid and glycolic acid are used, the amount of the lactic and glycolic acid units is from about 1 to about 97 mole %, desirably from about 20 to about 80 mole %, and preferably from about 40 to about 60 mole % based upon the total moles of said lactic acid and said glycolic acid.

The alternate bulk polymerization, high temperature, acid catalyst, low pressure route as set forth in FIG. 9 also produces a random, statistical biodegradable polyester copolymer and only requires a catalyst since, of course, solvents are not required. The polymerization temperature is generally from about 50° C. to about 180° C., desirably from about 80° C. to about 150° C., and preferably from about 90° C. to about 110° C. In order to remove water generated by the reaction, a vacuum or low pressures are utilized such as from about 0 mm Hg to about 50 mm Hg, desirably from about 0 mm Hg to about 10 mm Hg, and preferably from about 0 mm Hg to about 3 mm Hg. Suitable catalysts include various protonic and Lewis acids such as those set forth herein above with para-toluenesulphonic acid and SnCl₂ being preferred. The amount of the catalyst is generally from about 0.01 to about 1.0 or to about 5.0 equivalents, desirably from about 0.03 to about 0.5 equivalents, and preferably from about 0.05 to about 0.1 equivalents based upon the total equivalents of all hydroxyacid monomers. The molecular weight of this route is generally the same as that of the multi-step reaction route of FIG. 5, and thus copolymers are produced generally having a number average molecular weight of from around 2,000 Da to about 40,000 Da, desirably around 5,000 kDa to preferably 32,000 Da, and more desirably from about 6,000 Da to about 25,000 Da, and most preferably from about 8,000 kDa to about 20,000 kDa. The yield of the above described process is generally high, such as from at least about 10 mole %, generally at least about 50 mole %, and preferably at least about 90 mole % of all of said hydroxyacid monomers and functionalized monomers being incorporated into a polymer. The reaction time is generally from about 2 hours to about 72 hours, desirably from about 24 hours to about 60 hours, and preferably from about 36 hours to about 48 hours.

If desired, the various biodegradable copolyesters can contain conventional additives in conventional amounts known to the art and to the literature such as light stabilizers, pigments, heat stabilizers, anti static agents, UV absorbers, antioxidants, and the like, as well as various inorganic fillers such as calcium carbonate, clay, silica, and the like.

The statistical random polyester copolymers as set forth in FIGS. 5 and 9 generally contain a halogen group that is bromo. The repeat unit containing the halogen is set forth on the left side of FIG. 10. This repeat bromo group can be reacted by three different routes to yield the same copolyester but wherein the bromo group is an iodo group, an azide group, or a thioacetate group, see right side of FIG. 10. For example, if the copolyester of either FIGS. 5 and 9 are desired to have a pendant iodo functional group thereon, a copolymer can be reacted with an alkali metal iodate compound with any group one metal iodide salt such as sodium iodide or potassium iodide, under an inert gas such as nitrogen and argon, from temperatures that range from −40° C. to 60° C., ideally from 25° C. to 30° C. The amount of azide relative to the brominated repeat unit can range from 1 to 5 but preferably from 1.5 to 2.5 equivalences.

Similarly, if the bromine group set forth in FIGS. 5 and 9 of the copolyester are desired to be replaced by an azide group, the following reaction can be utilized. Any group with one metal azide salt such as sodium azide or potassium azide, can be reacted under an inert gas such as nitrogen and argon, from temperatures that range from −40° C. to 60° C., ideally from 0° C. to 25° C. The amount of azide relative to the brominated repeat unit can range from 0.5 to 1.5 equivalences but ideally is 0.75 to 0.95 equivalence.

If the bromo group on the copolyester polymers of FIGS. 5 and 9 are desired to be replaced with a thioacetate group, the following reaction can be utilized. With any group one metal thioacetate salt such as sodium thioacetate or potassium thioacetate can be reacted, under an inert gas such as nitrogen and argon, from temperatures that range from −20° C. to 70° C., ideally from 0° C. to 30° C. The amount of thioacetate relative to the brominated repeat unit can range from 0.5 to 1.5 equivalences but ideally is 0.75 to 1.5 equivalences.

The polymer system of the present invention has the advantage of a good leaving group (halogen) attached to the main chain of the biodegradable polymer. As noted above, the number of functional groups on the main chain of this biodegradable polymer can be varied by varying the feed ratio of the functionalized monomer such as 2-halo-3-hydroxypropionic acid monomer. The biodegradability of the polymer can also be tailored by varying the biomonomers such as lactic acid and glycolic acid feed ratios. Based an the ability of n-butylamine and pyridine to displace bromine from methyl 2-bromopropionate, and 4-amino-1-butanol and 5-amino-1-pentanol to displace the bromine end group from poly(methyl acrylate) (PMA), without reaction at the ester groups, functionalized PLGAs and other polyesters should be synthesized by reaction with the amine group of bioactive molecules. An example of potential application of this system is the covalent attachment of silver N-heterocyclic carbene (NHC) complexes developed by Youngs, et al, [Chem. Rev. 2005, 105, 3978-4008] at the halogen sites of the poly(halohydroxypropionic acid-co-lactic acid-co-glycolic acid) copolymer system. Previous NHCs have been shown to have antibacterial properties, and covalently attaching them would potentially give us a drug delivery device with slow release antibacterial properties,

The reference will be better understood by reference to the following examples which serve to illustrate, but not to limit the present invention.

EXAMPLES

Materials. 18-Crown-6 (Janssen 99%), diphenyl ether (Acros, 99%), glycolic acid (TCl, 98.0%), hydrobromic acid (Fluka,48 w/w % aq), D,L-lactic acid (Acros, 85%), potassium bromide (Acros, 98%), potassium thioacetate (Acros, 98%), D,L-serine (Alfa Aesar, 99%, sodium azide (Aldrich, 99%), sodium iodide (J. T. Baker), sodium nitrite (Sigma-Aldrich, 99.5%), succinonitrile (Sigma Aldrich, 99%) and p-toluenesutfonic acid monohydrate (pTSA; Aldrich, 98%) were used as received. Acetyl chloride (98%, Sigma-Aldrich) was distilled from PCl₅, Diethyl ether (ACS GR, MD) was distilled from purple sodium benzophenone ketyl under N₂. N,N-Dimethytformamide (ACS GR, ENID) was vacuum distilled from CaH₂ and stored over MgSO₄. Triethylamine (99.5%, Aldrich) was distilled from and stored over KOH under N₂. All other reagents and solvents were commercially available and were used as received.

Techniques. All reactions were performed under a N₂ atmosphere using a Schlenk line unless noted otherwise. ¹H and ¹³C NMR spectra (δ, ppm) were recorded on a Varian Mercury 300 (300 MHz and 75 MHz, respectively). Unless noted otherwise, all spectra were recorded in CDCl₃, and the resonances were measured relative to residual solvent resonances and referenced to tetramethylsilane. Number—(M_(n)) and weight average (M_(w)) molecular weights relative to linear polystyrene (GPC_(PSt)) and polydisperisties (pdi=M_(w)/M_(n)) were determined by gel permeation chromatography (GPC) from calibration curves of log M_(n) vs. elution volume at 35° C. using tetrahydrofuran (THF) as solvent(1.0 mL/min), a set of 50 Å, 100 Å, 500 Å, 10⁴ Å and linear (50-10⁴ Å) Styragel 5 μm columns, a Waters 486 tunable UV/Vis detector set at 254 nm, a Waters 410 differential refractometer, and Millenium Empower 2 software.

Example 1

Synthesis of 2-bromo-3-hydroxypropionic acid (FIG. 3). NaNO₂ (69 g, 1.0 mol) was added in 12 portions over three h to a cooled (−13° C.) solution of D,L-serine (53 g, 0.51 mol), potassium bromide (180 g. 1.5 mol), and hydrobromic acid (120 mL, 48 wt %, 1.0 moi) in distilled water (400 mL) that had been sparged with N₂; the solution turned brown upon addition of NaNO₂. The solution was warmed to room temperature (23° C.) and stirred for 16 h. It was then salted out with NaCl and extracted five tunes with ethyl acetate (100 mL ea). The aqueous layer was acidified with concentrated HBr to pH<2 and extracted five times with ethyl acetate (100 mL ea). The organic layers were combined and dried over MgSO₄. After filtration and removing the solvent by rotary evaporation, followed by drying under vacuum on a Schlenk line, the resulting yellow solid was recrystallized from CH₂Cl₂ to yield 55 g (64%) of 2-bromo-3-hydroxypropionic acid as a white crystalline solid; mp 48-51° C. ¹H-NMR (CDCl₃/DMSO-d₆): 3.58 (dd, CHH, ²J=11.6 Hz, ³J=5.9 Hz), 3.71 (dd, CHH, ²J=11.6, ³J=7.5 Hz), 3.99 (dd, CHBr, ³J=7.3, ³J=6.1 Hz). ¹³C NMR (CDCl₃/DMSO-d₆): 45.6 (CBr), 64.0 (COH), 171.0 (C═O).

Examples 2 and 3 relate to the preparation of a bromopropionate compound wherein the end groups contain an unreactable compound so that the a group therein can be replaced with an iodo group or with an azido group as set forth respectively, in Examples 5 and 6. Example 4 relates to the rearrangement of the bromo group in the model compound. Thus, Examples 4, 5, and 6 relate to actual reaction conditions, as utilized in FIG. 10, so that the above-noted bromo group can be replaced with either an iodo, an azide, or a thioacetate group.

Example 2

Synthesis of methyl 2-bromo-3-hydroxypropionate. Concentrated hydrobromic acid (10 drops) was added to a solution of 2-bromo-3-hydroxypropionic acid (10 g, 60 mmol) in methanol (80 mL, 2.0 mol). After refluxing the solution for 17 h, the solvent was removed using a rotary evaporator. The resulting oil was dissolved in CH₂Cl₂ (150 mL), and washed twice with aq NaHCO₃ (75 mL ea) and once with brine (100 mL). The organic layer was dried over MgSO₄. After filtration, the solvent was removed by rotary evaporation, and the residue was distilled (105-110° C./4 mm Hg) to yield 8.7 g (79%) of methyl 2-bromo-3-hydroxypropionate as a yellow oil. ¹H NMR: 2.22 (br s, OH), 3.83 (s, CH₃), 3.95 (dd, CHHOH, ²J=12.0 Hz, ³J=5.5 Hz), 4.06 (dd, CHHOH, ²J=12.1 Hz, ³J=7.4 Hz), 4.36 (dd, CHBr, ³J=5.6 Hz, ³J=7.4 Hz). ¹³C NMR: 44.4 (CHBr), 53.4 (CH₃), 63.8 (CH₂OH), 169.6 (C═O).

Example 3

Synthesis of methyl 3-acetoxy-2-bromopropionate. A solution (total volume 10 mL) of acetyl chloride (4.2 mL, 31 mmol) in dry ether was added dropwise to an ice-cooled solution of methyl 2-bromo-3-hydroxypropionate (4.6 g, 25 mmol) and triethylamine (4.2 mL, 30 mmol) in dry ether (5 mL). The reaction was then warmed to room temperature (23° C.) and stirred for 16 h. The reaction was poured into ice water (200 mL) and extracted four times with ether (50 mL ea). The organic layers were combined and dried over MgSO₄. After filtration, the solvent was removed by rotary evaporation, and the yellow residue was distilled (84-85° C./3 mm Hg) to yield 3.6 g (63%) of methyl 3-acetoxy-2-bromopropionate as a colorless oil. ¹H NMR: 2.08 (s, CH₃CO₂), 3.82 (s, CH₃O₂C), 4.50-4.38 (m, CH₂CHBr). ¹³C NMR: 20.8 (CH₃CO₂), 40.4 (CHBr), 53.4 (CH₃O₂C), 64.2 (CH₂), 168.3 (CH₃CO₂), 170.21 (CO₂C H₃).

Example 4

Synthesis of methyl 2-acetoxy-2-bromomethylethanoate. A solution of methyl 3-acetoxy-2-bromopropionate (0.27 g, 1.2 mmol) in succinionitrile (1.0 g, 12 mmol) was stirred and heated at 120° C. in a pressure tube for 72 hours. The product was 64% rearranged by ¹H NMR integration. ¹H NMR: 5.42 (t, CHCH₂Br), 4.46 (m, CH₂CHBr), 3.80 (q, CO₂CH₃), 3.71 (t, CHCH₂Br), 2.20 (s, CH₃CO₂). ¹³C-NMR: 169.90 (C(O)OCH₃), 167.56 (CH₃C(O)), 71.31 (CH), 52.91 (OCH₃), 29.61 (CH₂Br) 20.51 (CH₃C(O)).

Example 5

Synthesis of methyl 3-acetoxy-2-iodopropionate. A mixture of methyl 3-acetoxy-2-bromopropionate (0.12 g, 0.52 mmol) and sodium iodide (0.16 g, 1.1 mmol) in acetone (1 mL) was stirred at room temperature (23° C.) for 6 h. It was then poured into H₂O (10 mL) and extracted five times with CH₂Cl₂ (3 mL ea). The organic layers were combined, washed with aq Na₂S₂O₃ (10 mL), and dried over MgSO₄. After filtration, the solvent was removed by rotary evaporation to yield 0.12 g (86%) of methyl 3-acetoxy-2-iodopropionate as light yellow oil. ¹H NMR: 2.00 (s, CH₃CO₂), 3.72 (s, CH₃O₂C), 4.47-4.35 (m, CH₂CHI). ¹³C NMR: 14.3 (CHI), 20.8 (CH₃CO₂), 53.3 (s, CH₃O₂C), 65.7 (CH₂), 170.0 (CO₂CH₃), 170 0 (CH₃CO₂).

Example 6

Synthesis of methyl 3-acetoxy.2-azidoprepionate. A solution of methyl 3-acetoxy-2-bromopropionate (0.11 g, 0.49 mmol) and sodium azide (32.0 mg, 0.49 mmol) in dry DMF (1 mL) was stirred at room temperature (23° C.) for 45 min, and then poured into brine (10 mL) and extracted three times with CH₂Cl₂ (4 mL ea). The combined organic layers were dried over Na₂SO₄. After filtration, the solvent was removed by rotary evaporation to yield 50 mg (54%) of methyl 3-acetoxy-2-azidopropionate as slightly yellow oil. ¹H-NMR: 2.03 (s, CH₃CO₂), 3.77 (s, CH₃O₂C), 4.06 (dd, CHN₃, ³J=5.6, ³J=4.2 Hz), 4.32 (dd, CHH, ²J=11.6 Hz, ³J=5.8 Hz), 4.40 (dd, CHH, ²J=11.6, ³J=4.1 Hz). ¹³C NMR: 20.7 (CH₃CO₂), 53.2 (CH₃O₂C), 60.4 (CHN₃), 63.6 (CH₂), 168.3 (CO₂CH₃), 170.4 (CH₃CO₂).

Example 7

Synthesis of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)] in solution using carbodiimide coupling (FIG. 5). A mixture of D,L-lactio acid (0.69 g, 6.7 mmol), 2-bromo-3-hydroxypropionic acid (0.28 g, 1.7 mmol) and pTSA (50 mg, 0.29 mmol) in a sealed Schlenk tube was stirred at 110° C. under reduced pressure (˜1-3 mm Hg) for 14 h to create a prepolymer with M_(n)=8.81×10³, pdi=2.15. The Schlenk tube was removed from the oil bath, opened to the atmosphere, and its contents were dissolved in CH₂Cl₂ (60 mL). Half of the contents were transferred to a 50 mL round bottom flask. The solvent was refluxed over oven-dried 4 Å molecular sieves for 18 h to dehydrate the, polymer solution. After cooling the polymerization solution to room temperature, DPTS (0.10 g, 0.34 mmol) was added, and the solution was further cooled to 0-5° C. using an ice bath and DIPC (0.20 g, 1.6 mmol) was added dropwise. The reaction was performed for 7 h at room temperature. The polymer was precipitated into methanol (50 mL). The methanol was carefully decanted from the precipitate, and the polymers was dried in vacuo. The polymer was reprecipitated four times from CH₂Cl₂ (10 mL) into methanol (50 mL) to yield 0.23 g (52%) of halogenated PLA as a white powder; M_(n)=1.53×10⁴, pdi=1.71. ¹H-NMR: 1.8-1.4 (m, CH₃), 4.7-4.4 (m, CHBrCH₂), 5.30-5.10 (m, CHCH₃). ¹³C NMR: 16.62 (CH₃), 39.78 (CBr), 64.49 (CH₂CHBr), 68.95 (CHCH₃), 166.63 (CHBrCO₂), 169.33 (C(CH₃)COO).

Example 8

Synthesis of poly[(lactic acid)-co-(glycolic acid)-co-(2-bromo-3-hydroxypropionic acid)]]by direct polyesterification (FIG. 9). A solution of D,L-lactic acid (0.93 g, 9.0 mmol), glycolic acid (85 mg, 1.1 mmol), 2-bromo-3-hydroxypropionic acid (0.19 g, 1.1 mmol) and pTSA (51 mg, 0.29 mmol) in diphenyl ether (1 ml) in a Schlenk tube was stirred at 95° C. under reduced pressure (˜1-3 mm Hg) for 48 h. The Schlenk tube was removed from the oil bath, opened to the atmosphere, and its contents were dissolved in CH₂Cl₂ (10 mL). The Schlenk tube was cooled to −10° C., and the crystallized diphenyl ether was filtered off. The polymer was precipitated into methanol (50 ml), the solvents decanted, and the product was reprecipitated four times from CH₂Cl₂ (10 mL) into methanol (50 ml) to yield 0.53 g (53%) of halogenated PLGA as a white powder; M_(n)=2.37×10⁴, pdi=2.51. ¹H-NMR: 1.4-1.8 (m, CH₃), 4.4-4.7 (m, CHBrCH₂), 4.7-4.9 (m, CH₂CO₂), 5.10-5.30 (m, CHCH₃). ¹³C NMR: 16.6 (CH₃), 39.4 (CBr), 60.7 (CH₂CO₂), 64.5 (CH₂CHBr), 69.0 (CHCH₃), 166.5 (CH₂CO₂), 166.5 (CHBrCO₂), 169.0 (C(CH)COO).

Example 9

Partial isomerization of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)] to poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)-co-(2-bromomethyl-2-hydroxyethanoic acid)]. A solution of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid) (M_(n)=5.2×10⁴, pdi=1.66; 0.10 g, 0.42 mmol Br) in acetonitrile (0.8 mL) in a Schlenk tube was degassed by three freeze-pump-thaw (20 min pumping) cycles. The tube was backfilled with nitrogen and placed in an oil bath at 105° C. for 96 hours. ¹H NMR spectroscopy demonstrated that 25% of the 2-bromo-3-hydroxypropionate units rearranged to 2-brornomethyl-2-hydroxyethanoate units.

Example 10

Synthesis of poly[(lactic acid)-co-(3-hydroxy-2-iodopropionic acid)] (see FIG. 10). A solution of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)] (M_(n)=9.50×10³, pdi=1.42; 0.40 g, 1.3 mmol Br) and sodium iodide (0.17 g, 1.1 mmol) in acetone (1 mL) and stirred at room temperature (23° C.) for 48 h. The reaction mixture was diluted with CH₂Cl₂ (10 mL), washed once with water (10 mL), and precipitated into ice-cooled i-propanol (200 mL) to yield 0.43 g (94%) of copolymer as a yellow solid; M_(n)=8.45×10³, pdi=1.41. ¹H NMR: 1.4-1.7 (m, CH₃), 4.4-4.6 (m, CH₂CHI), 5.3-5.1 (m, CHCH₃). ¹³C NMR: 13.2 (CHI), 16.6 (CH₃), 66.0 (CH₂), 69.0 (CHCH₃), 168.3 (CHBrCO₂), 168.8 (CHICO₂), 169.2 (C(CH₃)COO).

Example 11A

Synthesis of poly[(lactic acid)-co-(3-hydroxy-2-azidopropionic acid)] (see FIG. 10) starting from the brominated copolymers. A solution of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)] (M_(n)=9.50×10³, pdi=1.42; 0.20 g , 0.62 mmol Br) and sodium azide (36 mg, 0.56 mmol) in dry DMF (1 mL) and stirred at room temperature (23° C.) for 48 h. The reaction mixture was diluted with CH₂Cl₂ (10 mL), washed once with water (10 mL), and precipitated into ice-cooled i-propanol (200 mL) to yield 0.11 g (62%) of copolymer as a yellow solid; M_(n)=1.56×10³, pdi=1.71. ¹H NMR: 1.4-1.7 (m, CH₃), 4.2-4.3 (m, CHN₃), 4.4-4.6 (m, CH ₂), 5.3-5.1 (m, CHCH₃). ¹³C NMR: 16.6 (CH₃), 39.6 (CHBr), 60.0 (CHN₃), 64.2 (CH₂), 69.1 (CHCH₃), 166.8 (CHBrCO₂) 169.3 (C(CH₃)COO), 173.2 (CHN₃CO₂).

Example 11B

Synthesis of poly[(lactic acid)-co-(3-hydroxy-2-azidopropionic acid)] (see FIG. 10) starting from the iodinated copolymer. A solution of poly[(lactic acid)-co-(2-iodo-3-hydroxypropionic acid)] (M_(n)=8.45×10³, pdi=1.41; 0.11 g, 0.12 mmol l) and sodium azide (13 mg, 0.21 mmol) in dry DMF (1 mL) and stirred at roam temperature (23° C.) for 48 h. The reaction mixture was diluted with CH₂Cl₂ (10 mL), washed once with water (10 mL), and precipitated into ice-cooled i-propanol (200 mL) to yield 0.13 g (87%) of copolymer as a yellow solid; M_(n)=1.97×10³, pdi=1.41.

Example 11C

Synthesis of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)-co-(2-acetylthiomethyl-2-hydroxyethanoic acid)] (see FIG. 10) starting from the brominated copolymer. A solution of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)] (M_(n)=9.50×10³, pdi=1.42; 0.20 g, 0.60 mmol Br), potassium thioacetate (65 mg, 5.7 mmol) and 18-crown-6 (29 mg, 0.10 mmol) in acetonitrile (2 mL) was stirred at room temperature (23° C.) for 48 h. The reaction mixture was diluted with CH₂Cl₂ (10 mL), washed one with water (10 mL), and, precipitated into ice-cooled i-propanol (120 mL) to yield 58 mg (30%) of copolymer as a transparent glassy solid; M_(n)=1.50×10³, pdi=1.28. ¹H NMR: 1.4-1.7 (m, CH₃), 2.3 (s, CH₃COS), 3.2-3.4 (m, CHCH₂S), m, 4.3-4.6 (CH₂CHBr), 5.1-5.2 (m CHCH₃). ¹³C NMR: 16.6 (CH₃), 30.0 (SCOCCH₃), 39.7 (CBr), 45.0 (CS), 64.5 (CH₂CHBr), 69.0 (CHCH₃), 70.0 (CH₂CHS), 166.5 (CHBrCO), 169.2 (C(CH)COO), 173.2 (SCO).

Example 11D

Synthesis of poly[(lactic acid)-co-(2-iodo-3-hydroxypropionic acid)-co-(2-acetylthiomethyl-2-hydroxyethanoic acid)] starting from the iodinated copolymer. A mixture of poly[(lactic acid)-co-(2-iodo-3-hydroxypropionic acid)] (M_(n)=8.45×10³, pdi=1.41; 0.10 g, 0.22 mmol l), potassium thioacetate (22 mg, 0.22 mmol) and 18-crown-6 (10 mg, 40 μmol) in acetonitrile (1 mL) was stirred at room temperature for 48 h. The reaction mixture was diluted with CH₂Cl₂ (10 mL), washed once with water (10 mL), and precipitated into ice-cooled i-propanol (120 mL) to yield 0.13 g of copolymer as a yellow solid; M_(n)=1.70×10³, pdi=1.35.

Example 11E

Synthesis of poly[(lactic acid)-co-(2-bromo4-hydroxypropionic acid)-co-(2-azidomethyl-2-hydroxyethanoic acid)] starting from the isomerized brominated copolymer. A solution of sodium azide (17 mg, 0.26 mmol) in dry DMF (15 mL) was added dropwise over 30 minutes to a solution of poly(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)-co-(2-bromomethyl-2-hydroxyethanoic acid)] (M_(n)=9.50×10³, pdi=1.42: 0.20 g, 0.21 mmol CH₂Br) in DMF (2 mL) and stirred at room temperature for 48 h. The reaction was concentrated using a rotary evaporator and then dissolved in CH₂Cl₂ (10 mL), washed once with water (10 mL), and the organic layer was concentrated using a rotary evaporator to yield 0.11 g (58%) of copolymer as a white solid; M_(n)=3.93×10³, pdi1.86. ¹H NMR: 1.4-1.7 (m, CH₃), 2.4 (m, CHCH₂N₃), 3.6-3.7 (m, CH₂N₃), m, 4.1-4.3 (m, CHCH₂Br), 4.3-4.6 (CHBr), 5.1-5.2 (m CHCH₃), 5.3-5.4 (m, CH₂Br). ¹³C NMR: 16.6 (CH₃), 29.0 (CHCH₂Br), 39.7 (CHBr), 60.0 (CHCH₂N₃), 64.4 (CH₂CHBr), 66.6 (CHCH₂N₃) 70.0 (CHCH₃), 165.5 (CHCH₂CO), 166.7 (CHBrCO), 169.3 (C(CH₃)COO).

Example 11F

Synthesis of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)-co-(2-acetylthiomethyl-2-hydroxyethanoic acid)] starting from the isomerized brominated copolymer. A solution of poly[(lactic acid)-co-(2-bromo-3-hydroxypropionic acid)-co-(2-bromomethyl-2-hydroxyethanoic acid)] (M_(n)=7. 06×10³, pdi=1.99; 0.20 g. 0.21 mmol CH₂Br), potassium thioacetate (23 mg, 0.20 mmol) and 18-crown-6 (8.5 mg, 32 μmol) in acetonitrile (35 mL) was stirred at room temperature (23° C.) for 48 h. The reaction mixture was concentrated on a rotary evaporator and then dissolved in CH₂Cl₂ (10 ml), and washed once with water (10 mL), to yield 0.27 g of copolymer as a yellow solid; M_(n)=3.57×10³, pdi=2.24. ¹H NMR: 1.4-1.7 (m, CH₃), 2.3 (s, CH₃COS), 4.3-4.6 (m, CHCH₂S, CH₂CHI), 5.1-5.2 (m CHCH₃). ¹³C NMR: 16.6 (CH₃), 30.0 (SCOCCH₃), 45.0 (CS), 66.0 (CH₂CHI), 66.6 (Cl), 69.0 (CHCH3), 70.0 (CH₂CHS), 166.5 (CHBrCO), 169.2 (C(CH₃)COO), 173.2 (SCO).

Results and Discussion

Polyesterification: Direct polycondensations in bulk are reversible reactions, and need extremely high extent of conversion to achieve high molecular weight. At higher conversions, the increase in the viscosity of the bulk, makes removal of the by-product, water, by heat and vacuum more and more difficult. Adding a small amount of high boiling solvent, like diphenylether (DPE), plasticizes the bulk, permitting the bulk to be dehydrated further. This shifts the equilibrium to the right, and affords higher molecular weights. The number average molecular weights obtained were around 20,000 Da, measured by GPC calibrated to polystyrene standards. However, since the different co-polymer compositions have different molecular weights, the co-polymerizations may only be compared by their degree of polymerizations. PLA had the highest DP. Upon introducing glycolic acid, the PLGA copolymers formed with lower DP. Co-polymers of lactic acid with 2-bromo-3-hydroxypropionic acid also formed polymers with lower DP than that of PLA and PLGA. Increasing content of 2-bromo-3-hydroxypropionic acid led to polymers with decreasing DP. This could be attributed to the lower reactivity of 2-bromo-3-hydroxypropionic acid, as compared to LA. However, with the tri-component co-polymers of LA, GA and 2-bromo-3-hydroxypropionic acid of varying ratios, their DP was higher than the copolymers of just LA with 2-bromo-3-hydroxypropionic acid. This could be because of the higher reactivity of GA units. The polydispersity was also higher in the tri-component co-polymers.

Reactions on the model compound: (Table 2) To investigate potential reactions to functionalized the brominated polyester, a small molecule model, methyl 3-acetoxy-2-bromopropanoate, was synthesized by esterifying the carboxylic acid and the hydroxyl groups of 2-bromo-3-hydroxypropionic acid with methanol and acetyl chloride respectively. This molecule and the brominated polyester have very similar reactivity at the halogen, as the immediate electronic environment of the carbon-halogen bond in the model and the polymer is identical out to three bonds. The model molecule underwent substitution at the halogen using sodium azide, sodium iodide and sodium thioacetate as nucleophiles to prepare the azido, iodo and thioester derivatives. These reactions were fast, less than 1 hour in the case of azide, and quantitative. Highly efficient functionalization reactions are necessary for post-polymerization functionalization as bimolecular reactions with macromolecules occur much slower than those with small molecules, due to diffusion limitations, and non-reacted sites along the backbone cannot be removed post reaction.

Potassium phenoxide and potassium acetate caused a competing α-elimination reaction that makes them unsuitable for substitution. Potassium phenoxide caused 95% elimination at room temperature in less than one hour, Potassium acetate caused varying amounts of elimination, 45-80%, depending on temperature and solvent, with lower temperatures and more polar solvents favoring substitution. Even a small amount of elimination makes these nucleophiles unsuitable for polymer functionalization because the elimination results in chain-scission. (scheme 4).

α to βHalo Rearrangement: While conducting substitution experiments using 3-methyl-4,5-dichloroimidazole, a poor nucleophile, and MABP a product was formed that did not correspond to substitution or elimination. Repeating this experiment in the absence of a nucleophile it was observed that MABP underwent a thermal rearrangement from the α-bromo isomer to β-bromo isomer, likely via a five-member ring intermediate.

This rearrangement is supported by ¹H and ¹³C NMR spectroscopy, which shows the emergence of resonances corresponding to the methine at 5.43 and 71.38 ppm and the methylene at 3.71 and 29.68 ppm in the 1H and ¹³C spectra respectively, of the β-bromo isomer.

This rearrangement mechanism is further supported by an experiment isomerizing a 5.2 kDa 58:42 poly[(lactic acid)-co-(2bromo-3-hydroxypropionic acid)]. The polyester was heated to 105° C. in acetonitrile for 96 hours and observed to isomerize 25% with very little loss in molecular weight, as observed by a shift in GPC retention time from 39.9 to 40.9 minutes. This shift may be accounted for by a change in hydrodynamic due to the different repeat unit and not actual polymer degradation.

This rearrangement proceeds most efficiently upon heating in polar solvent, acetonitrile, succinonitrile or DMF. The rearrangement of the small molecule proceeded to an equilibrium concentration of 60:40β to α, quantified by ¹H-NMR at 120° C. in succinonitrile in a pressure tube. This thermal rearrangement offers a possible route to orthogonal functionalization by providing two types of halogen functionality, a primary halogen, which is more susceptible to nucleophilic substitution due to reduced steric bulk at the σ* orbital, and an α-halo ester, capable of radical chemistry due to the adjacent carbonyl, in the same polyester backbone utilizing one functional monomer. Furthermore, this isomerization can be accomplished in situ during the polycondensation and the amount of each isomer repeat unit controlled by the temperature used during the polymerization. Below 95° C. almost no β-halo isomer is observed.

Reactions on the Polyester: (Table 2) The reactions on the polyester all were ran for 48 hours at room temperature. Iodo and azide both substituted quantitatively, while the thioaceate showed substitution once the polymer had rearranged to the β halogen form. In the case of iodo substitution there was a loss of 1,000 Mn when substitution occurred. When the thioacetate substitutes onto the polymer there is a loss of 8,000 and 7,800 Da from the bromo and iodo derivatives respectively. When sodium azide substitutes onto the polymer 7,900 and 7,900 Da from the bromo and iodo derivatives respectively. Looking at the molecular weight differences the iodo polymer is better for functionalizing, which corresponds with iodine being a better leaving group then bromine.

In order to decrease the loss of molecular weight when functionalizing the polyester a partially isomerized polymer was used. By targeting the primary halide the favorability of nucleophlic substitution is increased. For the sodium azide substitution a slow dilute addition of sodium azide resulted in a % M_(n) loss of 33% which is an improvement from 84% when the alpha bromine is targeted. The reason for this improvement is that there is a primary halide that favors S_(n)2 over E₂. Another reason is presumably that the polymer exists as a random coil in solution and so the bromine in the center of the coil is shielded from the azide. This causes a local concentration of azide on the outside of the polymer to be in excess of 1.0 and increases the chance of elimination. With the dilute addition the azide the excess azide at the surface of the polymer is avoided, and substitution is favored. When the partially isomerized polymer is substituted with thioacetate the % M_(n) loss decreases from 89% to 47%. This is because the thioacetate does not have to wait for the polymer to spontaneously rearrange before it substitutes. This limits the amount of excess thioaceate in the system and again promotes substitution over elimination.

TABLE 1 Feed Ratio GPC PSt by NMR calculation Sample LA GA BrH Mn Mw PDI DP LA GA BrH PLA 100 0 0 3.16 × 10⁴ 5.12 × 10⁴ 1.62 438.9 100 0 0 PLGA9010 90 10 0 2.92 × 10⁴ 3.49 × 10⁴ 1.53 324.4 90.1 9.9 0 PLGA8020 80 20 0 2.01 × 10⁴ 3.05 × 10⁴ 1.51 290.5 80.3 19.7 0 PLBr9010 90 0 10 2.08 × 10⁴ 4.13 × 10⁴ 1.99 260.3 89.9 0 10.1 PLBr8020 80 0 20 1.80 × 10⁴ 3.96 × 10⁴ 2.2 205.0 80.3 0 19.7 PLBr7030 70 0 30 1.68 × 10⁴ 3.67 × 10⁴ 2.18 175.5 70.3 0 29.7 PLBr6040 60 0 40 1.71 × 10⁴ 3.44 × 10⁴ 2.01 165.1 59.7 0 39.3 PLBr5050 50 0 50 2.03 × 10⁴ 3.91 × 10⁴ 1.93 182.1 50 0 50 PLGBr801010 80 10 10 2.99 × 10⁴ 7.49 × 10⁴ 2.51 380.9 80.1 10 9.9 PLGBr701020 70 10 20 2.37 × 10⁴ 9.45 × 10⁴ 3.99 274.3 70 10.1 19.9 PLGBr601030 60 10 30 2.30 × 10⁴ 1.00 × 10⁵ 4.35 243.9 60.1 10 29.9 PLGBr702010 70 20 10 2.32 × 10⁴ 5.87 × 10⁴ 2.52 300.9 69.8 20.1 9.1 PLGBr602020 60 20 20 2.20 × 10⁴ 9.10 × 10⁵ 4.13 258.9 59.46 16.29 24.25 PLGBr502030 50 20 30 1.89 × 10⁴ 7.28 × 10⁵ 3.86 202.9 51.64 16.52 31.84

TABLE 2 Mn Mn pdi pdi Reactant Solvent Time Temp Conversion before after before after Model sodium Acetone 6 h RT quatitative iodide sodium DMF 45 min RT quatitative azide sodium Acetonitrile 48 h RT re-arranged thioacetate substituted Brominated sodium Acetone 48 h RT quatitative 9470 8450 1.42 1.41 iodide Polyester sodium DMF 48 h RT quatitative 9470 1560 1.42 1.71 azide sodium Acetonitrile 48 h RT re-arranged 9470 1500 1.42 1.28 thioacetate substituted Iodated sodium DMF 48 h RT quatitative 8450 1970 1.41 1.48 azide Polyester sodium Acetonitrile 48 h RT re-arranged 8450 1700 1.41 1.35 thioacetate substituted Partially sodium DMF 24 h RT quatitative 5850 3925 2.11 1.86 Isomerized azide Brominated sodium Acetonitrile 48 h RT re-arranged 7060 3751 1.99 2.24 polyester thioacetate

The functionalized copolyesters of the present invention have the same end uses of that of current commercial biodegradable polyesters. For example, they can be utilized to make food trays, cold drink cups, packaging applications, bottles, jars, pots, films, bags, and so forth. They also can be utilized as a feedstock for attachment of medical or drug delivery systems or compounds thereto.

While in accordance with the patent statutes the best mode and preferred embodiment have been set forth, the scope of the invention is not intended to be limited thereto, but only by the scope of the attached claims. 

What is claimed is:
 1. A functionalized biodegradable copolyester, comprising; repeat units derived from one or more diols containing from 2 to about 10 carbon atoms and one or more dicarboxylic acids containing from 2 to about 15 carbon atoms, or repeat units derived from one or more hydroxyacids containing from 2 to about 20 carbon atoms, or both; repeat units derived from one or more functionalized hydroxyacids; and wherein said copolyester is a random, statistical copolymer and is biodegradable.
 2. The functionalized biodegradable copolyester of claim 1, wherein the amount of said functionalized repeat units is from about 10 to about 99 mole %; and wherein said hydroxyacid comprises glycolic acid, galactaric acid, hydroxypropionic acid, lactic acid, hydroxybutyric acid, hydroxyisobutyric acid, hydroxy methylbutyric acid, bis(hydroxymethyl)propionic acid, gibberellic acid, hydroxyoctadecanoic acid, di-tert-butyl hydroxybenzoic acid, benzilic acid, hydroxyl fluorenecarboxylic acid, hydroxydecanoic acid, hydroxynaphthalenecarboxylic acid, hydroxybenzenedicarboxylic acid, hydroxymethylbenzoic acid, hydroxyphenylacetic acid, mandelic acid, hydroxymethoxybenzoic acid, methoxysalicylic acid, hydroxyoctanoic acid, hydroxycinnamic acid, dihydroxycinnamic acid, dihydroxyhydrocinnamic acid, hydroxyphenylpropionic acid, dihydroxytartaric acid, hydroxymethoxycinnamic acid, salicylic acid, citrazinic acid, galacturonic acid, glucuronic acid, hydroxypropanedioic acid, hydroxyphenyl propionic acid, methoxysalicylic acid, tartaric acid, or trihydroxybenzoic acid, or any combination thereof.
 3. The functionalized biodegradable copolyester of claim 2, wherein said functionalized hydroxyacid is HHPPA, chlorohydroxybenzoic acid, chloromandelic acid, chlorosalicylic acid, dibromo hydroxybenzoic acid, dichlorohydroxy benzoic acid, dichlorosalicyclic acid, a hydroxyacid containing a halogen group other than said preceding acids, a hydroxyacid containing an azide group, or a hydroxyacid containing a thioacetate group, or any combination thereof.
 4. The functionalized biodegradable copolyester of claim 3, wherein the amount of said functionalized repeat units is from about 30 to about 80 mole %; wherein the number average molecular weight of said copolyester is from about 2,000 to 40,000 Da; and wherein said functionalized group is said halogen, said azide, or said thioacetate.
 5. The functionalized biodegradable copolyester of claim 4, including repeat units derived from said lactic acid, or said glycolic acid, or both.
 6. The functionalized biodegradable copolyester of claim 5, wherein said number average molecular weight of said copolyester is from about 6,000 to about 25,000 Da; and wherein said functional group exists on the backbone of said copolyester.
 7. The functionalized biodegradable copolyester of claim 6, wherein the amount of said functionalized monomer is from about 35 to about 50 mole %; including said repeat units derived from said lactic acid and including said repeat units derived from said glycolic acid, and wherein the amount of said lactic acid and said glycolic repeat units is from about 20 to about 80 mole % based upon the total number of said lactic acid and said glycolic acid repeat units.
 8. A process for synthesizing a functionalized biodegradable copolyester comprising the steps of: reacting one or more diols containing from 2 to about 10 carbon atoms with one or more dicarboxylic acids containing from 2 to about 15 carbon atoms, or reacting one or more hydroxyacids containing from 2 to about 20 carbon atoms, or both; with one or more functionalized hydroxyacids at low pressure and elevated temperature in the presence of a protonic acid catalyst or a Lewis acid catalyst.
 9. The process of claim 8, wherein said pressure is about 50 mm Hg or less; wherein said temperature is from about 50° C. to about 180° C; and wherein said hydroxyacid comprises glycolic acid, galactaric acid, hydroxypropionic acid, lactic acid, hydroxybutyric acid, hydroxyisobutyric acid, hydroxy methylbutyric acid, bis(hydroxymethyl)propionic acid, gibberellic acid, hydroxyoctadecanoic acid, di-tert-butyl hydroxybenzoic acid, benzilic acid, hydroxyl fluorenecarboxylic acid, hydroxydecanoic acid, hydroxynaphthalenecarboxylic acid, hydroxybenzenedicarboxylic acid, hydroxymethylbenzoic acid, hydroxyphenylacetic acid, mandelic acid, hydroxymethoxybenzoic acid, methoxy salicylic acid, hydroxyoctanoic acid, hydroxycinnamic acid, dihydroxycinnamic acid, dihydroxyhydrocinnamic acid, hydroxyphenylpropionic acid, dihydroxytartaric acid, hydroxymethoxycinnamic acid, salicylic acid, citrazinic acid, galacturonic acid, glucuronic acid, hydroxypropanedioic acid, hydroxyphenyl propionic acid, methoxy salicylic acid, tartaric acid or trihydroxybenzoic acid or any combination thereof.
 10. The process of claim 9, wherein the amount of said functionalized hydroxyacid is from about 30 to about 80 mole % based upon the total number of moles of said one or more functionalized hydroxyacids and said one or more non-functionalized hydroxyacids; and wherein the number average molecular weight of said functionalized biodegradable copolyester is from about 2,000 Da to about 40,000 Da.
 11. The process of claim 10, wherein said pressure is about 10 mm Hg or less; and wherein said functionalized hydroxyacid is HHPPA, chlorohydroxybenzoic acid, chloromandelic acid, chlorosalicylic acid, dibromo hydroxybenzoic acid, dichlorohydroxy benzoic acid, dichlorosalicyclic acid, a hydroxyacid containing a halogen group other than said preceding acids, a hydroxyacid containing an azide group, or a hydroxyacid containing a thioacetate group, or any combination thereof.
 12. The process of claim 11, wherein said catalyst comprises p-dimethylaminopyridinium toluenesulphonate (DPTS), p-toluidine hydrochloride, dimethyl-p-phenylenediamine dihydrochloride, p-toluenesulphonic acid, or SnCl₂, or any combination thereof.
 13. The process of claim 12, wherein the amount of said one or more functionalized hydroxyacids are from about 35 to about 50 mole %; including said repeat units derived from said lactic acid or including said repeat units derived from said glycolic acid, or both, and wherein the amount of said lactic acid repeat units is from about 20 to about 80 mole % based upon the total number of said lactic acid and said glycolic acid repeat units; and wherein catalyst is p-toluene sulphonic acid.
 14. The process of claim 8, including further reacting said biodegradable functionalized copolyester with a linking agent and a protonic catalyst or a Lewis acid catalyst at ambient temperature.
 15. The process of claim 11, including further reacting said biodegradable functionalized copolyester with a linking agent and a protonic catalyst or a Lewis acid catalyst at ambient temperature. 